Veneer Restoration Glass Ceramics
Veneer Restoration Glass Ceramics

Veneer Restoration Glass Ceramics

Flexural Strength
350-450Mpa
Chemical Solubility
≤100μg/mm³
Vickers Hardness
above 5400Mpa
Density
2.4~2.6g/cm³
Country of origin
Changsha China
Brand Name
Hongchon
Power type
Power type
Warranty service
1years
After-sales service
Online technical support
Material
ceramics
Shelf life
1years
Certification
CE
Medical device classification
Class II
MOQ
5 piece
Package
5 piece per box
OEM/ODM
Acceptable
Used
Dental Lab

1.product Introduction

Veneer restoration glass ceramics play an important role in making excellent all ceramic aesthetic restoration. Veneer restoration glass ceramics can bring you simplified preparation steps, more aesthetic restorations, easier fabrication techniques to support experienced laboratory production and improve laboratory economy.

Veneer restoration glass ceramics  is an innovative lithium disilicate glass-ceramic that has optimized translucency, durability and strength for full anatomical restorations.

Veneer restoration glass ceramics  is a material used to obtain restorations through traditional investment casting technology. With different dyeing, back-cutting or porcelain decoration processes, it can produce crystal-clear restorations. Glass Ceramics Pressing Ingots Lithium Disilicate Dental Material are suitable for a variety of aesthetic restoration indications and is also a micro-porcelain restoration. The material of choice for application in minimally invasive cosmetic dentistry.

2.product Parameter (specification)


Technical ParametersChemical Compositions

Flexural Strength

350-450Mpa

SiO₂

58.5-72.5%

Chemical Solubility

≤100μg/mm³

Li₂O

13-15%

Vickers Hardness

above 5400Mpa

K₂O

3-5%

Density

2.4~2.6g/cm³

Other Oxides

7.5-25%

There are characteristics of HT(which means high translucency), LT(which means low translucency) and MO(which means medium opacity). It has widely applicable colors for you to choose from. 

Size

Translucent

Pieces/Box

Available Shades

D13×10

HT

10pcs

A1/A2/A3/B1/B2/C1/BL1/BL2/BL3

LT

10pcs

A1/A2/A3/B1/B2/C1/C2/BL1/BL2/BL3

MO

10pcs

MO1

 

3.Advantage:

1. High aesthetic restoration effect.

2. Superior chemical stability and bending strength.

3. Easy to cut and extend the service life of the bur.

4. Simple and fast crystallization process to reduce operating time.

5. Unique color change characteristics ensure perfect repair effect.

 

4.Recommended Pressing Procedures:

Press item

Investment Ring System

B

T

℃/min

T

H

min

E

μm/min

LT / MO

100g

700

60

913

15

250

HT

100g

700

60

910

15

250

5.Product  application

Veneer Restoration Glass Ceramics(图1)




6.Product packaging

Veneer Restoration Glass Ceramics(图2)

Porcelain veneers are bonded to the surface of the teeth using press ingots that can improve the color, shape, and contours of the teeth without the need for significant cuts in tooth tissue. It can reduce damage and cuts to teeth, retain the structure and function of original teeth to the greatest extent, help reduce patient discomfort, shorten treatment time, and provide longer-lasting repair effects.

 