Anterior multilayer zirconia
Anterior multilayer zirconia

Anterior multilayer zirconia

Product Type
Multilayer zirconia
Colors
BL1 BL2 BL3 A1 A2 A3 A3.5 A4 B1 B2 B3 B4 C1 C2 C3 C4 D2 D3 D4
Aesthetic
ultra translucent
Sintered Density
6.0g/cm³
Bending Strength
700MPA to1050MPA
Light transmittance
45% to 57%
Sintering Temperature
1500℃
Model Number
OD98 / OD95 / AG 92*75 /
Product Size
10mm / 12mm / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm

 Anterior multilayer zirconia(图1)

Anterior multilayer zirconia(图2)

         

FEATURES

·Suitable for anterior and posterior restoration

·6layers Multilayer color

·Best translucency with strong strength






RECOMMENDED INDICATIONS

Anterior multilayer zirconia(图3)

AVAILABLE SHADES

Anterior multilayer zirconia(图4)

Anterior multilayer zirconia(图5)


Anterior multilayer zirconia(图6)



Anterior multilayer zirconia block with full contour material has the natural gradient of color, translucency, and strength in a real sense.


The full contour zirconia material is closer to natural teeth than other materials from the view of aesthetics. Also, its abrasion makes it become a dental material with biomimetic properties.


The cervical strength of Anterior Multilayer Zirconia Block is up to 1200Pa, which is a great improvement. Long span bridges are stable, and it fully meets laboratories’ strength requirements for a broad range of indications.


The color transition of Anterior Zirconia Block with full contour zirconia is similar to natural teeth from cervical to incisal. Anterior Multilayer Zirconia Block Zir has a smooth color gradient without visible layers.


Anterior Zirconia Block is the leading digital solution in the field of Zirconia materials. The full contour zirconia with excellent characteristics is combined with the Anterior Rapid Aesthetic Solution, which will help laboratories finalize and deliver Zirconia restorations within 24 hours.


Multilayer zirconium oxide with natural esthetics,natural color and translucency gradient and high flexural strength (1200 MPa cervical, 800 MPa incisal).


These properties enable the fabrication of highly esthetic, monolithic single-tooth and bridge restorations in the anterior and posterior region. The specially adjusted translucency gradient ensures good coverage in the cervical area and increased translucency in the incisal area. The integrated color gradient also ensures the efficient fabrication of natural-looking restorations.