Fully Monolithic Zirconia
Fully Monolithic Zirconia

Fully Monolithic Zirconia

Product Type
Multilayer zirconia
Colors
Vita 16 color+BL1/BL2/BL3
Aesthetic
ultra translucent
Sintered Density
6.0g/cm³
Bending Strength
700MPA to1050MPA
Light transmittance
45% to 57%
Sintering Temperature
1500℃
Model Number
OD98 / OD95 / AG 92*75 /
Product Size
10mm / 12mm / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm

Fully Monolithic Zirconia(3D plus)Product Introduction:

Changsha Hongchuang Technology Co., Ltd., China's leading zirconium oxide manufacturer, is proud to launch its fully monolithic zirconium, also known as 3Dplus multi-layered zirconium. This is a cutting-edge restorative dental solution. Designed to achieve the perfect combination of strength and aesthetics, the product provides an ideal material for the manufacture of durable and visually appealing dental restorations.

Fully Monolithic Zirconia(图1)


Fully Monolithic Zirconia(3D plus) Product Parameter:

Color:

Vita 16 shades+BL1/BL2/BL3

Aesthetic:

Ultra Translucent

Sintered Density:

6.0g/cm³

Bending Strength:

700Mpa to 1050Mpa

Light Transmittance:

45% to 57%

Sintering Temperature:

1500℃

Recommend Indications:

Veneer & Inlay & Onlay & Partial Crown & Anterior Crown & Posterior Crown & Full Contour Bridge≤7 units

Fully Monolithic Zirconia(3D plus)size:

Fully Monolithic Zirconia(图2)

Chemical composition

Components

3D Plus ML

ZrO2+HfO2+Y2O3

≥99%

Y2O3

7.0%-10%

Al2O3

<0.15%

Other Oxides

<0.5%


Fully Monolithic Zirconia(3D plus) Multilayer Sintering Curve

Sintering step

Start Temperature(℃)

End Temperature(℃)

Time(Min)

Rate(℃/Min)

Step 1

20

900

91

9.7

Step 2

900

900

30

0

Step 3

900

1500

182

3.3

Step 4

1500

1500

120

0

Step 5

1500

800

60

-11.6

Please follow the sintering curve and notice the peek temperature is 1500℃. Any questions from you will be seriously treated and sincerely welcomed.


Fully Monolithic Zirconia(3D plus)Feature and Application:

Changsha Honchon Technology's Fully Monolithic Zirconia is designed for fabricating full-contour crowns, bridges, inlays, onlays, and veneers. Its high translucency mimics the depth and vitality of natural teeth, making it an excellent choice for anterior and posterior restorations. The material's robust mechanical properties ensure that it can withstand the occlusal forces of the oral environment, making it a reliable option for long-lasting dental solutions.


Fully Monolithic Zirconia(3D plus) Details:

The production process of Fully Monolithic Zirconia involves meticulous attention to detail, ensuring consistency in quality and performance. State-of-the-art manufacturing techniques are employed to achieve uniform density and shade throughout each zirconia blank. Changsha Honchon Technology's rigorous quality control system ensures that every batch of zirconia meets the company's exacting standards.


Fully Monolithic Zirconia(3D plus) Qualification:

Fully Monolithic Zirconia from Changsha Honchon Technology is certified to meet international standards for dental materials. It has undergone extensive testing to verify its biocompatibility, strength, and durability. Dental professionals can trust in the safety and reliability of this product for their restorative needs.

Fully Monolithic Zirconia(图3)


Delivery, Shipping, and Serving:

Changsha Honchon Technology is dedicated to providing exceptional customer service, from order processing to after-sales support. Products are securely packaged and shipped via reliable carriers to ensure they arrive in pristine condition. The company's customer service team is readily available to assist with any inquiries and to provide comprehensive support throughout the product's lifecycle.

Fully Monolithic Zirconia(图4)

FAQ:


Q1: Can Fully Monolithic Zirconia be used for long-span bridges?

A1: Yes, the high strength of Fully Monolithic Zirconia makes it suitable for long-span bridges, although case-specific considerations should be taken into account by the dental professional.


Q2: Is there a need for special equipment to mill Fully Monolithic Zirconia?

A2: Fully Monolithic Zirconia can be milled with standard CAD/CAM equipment designed for dental zirconia. However, it is recommended to use milling tools optimized for zirconia to ensure the best results.


Q3: How should restorations made from Fully Monolithic Zirconia be cemented?

A3: For cementing Fully Monolithic Zirconia restorations, it is recommended to use zirconia-compatible cements and follow the manufacturer's guidelines for surface preparation and cementation protocols.


Q4: Are there any specific maintenance requirements for Fully Monolithic Zirconia restorations?

A4: Fully Monolithic Zirconia restorations are low maintenance but should be cared for like natural teeth with regular brushing and flossing. It is also important for patients to attend regular dental check-ups.


Q5: How does the translucency of Fully Monolithic Zirconia compare to other dental ceramics?

A5: The translucency of Fully Monolithic Zirconia has been optimized to closely resemble that of natural tooth enamel, offering a more aesthetic alternative to traditional opaque zirconia while still providing superior strength.